Stability of dentin matrix treated with caffeic acid phenethyl ester at different concentrations

Aim: The aim of this study was to investigate the impact of pretreatment with ethanolic solutions of caffeic acid phenethyl ester (CAPE) at varying concentrations on the dentin collagen matrix, specifically focusing on its biomodification potential. This was assessed through evaluations of the modulus of elasticity and changes in mass. Methods: Seventy dentin collagen matrices (demineralized sticks) were prepared to receive treatments with ethanolic solutions of CAPE at concentrations of 0.05%, 0.1%, 0.5%, or 2.5%, or with control treatment solutions (distilled water or ethanol) for one hour. The dentin matrices were evaluated for modulus of elasticity and mass before (baseline), immediately after treatment (immediately), and after storage in Simulated Body Fluid (SBF) for time intervals of 1 and 3 months. Results: Generalized linear models for repeated measures over time indicated no significant differences between groups (p=0.7530) or between different time points (p=0.4780) in terms of the modulus of elasticity. Regarding mass variation, no differences were observed in the time interval between 1 month and the immediate time (p=0.0935). However, at the 3-month mark compared to the immediate time, the 0.1% CAPE group exhibited less mass loss compared to the water group (p=0.0134). Conclusion: This study concludes that various concentrations of CAPE in an ethanolic solution did not affect the modulus of elasticity of dentin, suggesting that CAPE lacks biomodifying potential in this context. However, it was observed that 0.1% CAPE positively influenced the variation in mass over different evaluation time intervals

Does the combination of whitening toothpaste and hydrogen peroxide bleaching increase the surface roughness and change the morphology of a nanofilled composite?

Aim: To evaluate changes in the surface roughness and morphology of a nanofilled composite following toothbrushing with a whitening (WT) or regular toothpaste (RT), alone or combined with 35% hydrogen peroxide bleaching (HP). Methods: Seventy disc-shaped nanofilled composite (Filtek Z350XT) specimens were randomly divided into groups (n=10): WT, RT, TB (without toothpaste ­ control) or the combinations WT/ HP, RT/HP, TB/HP and HP. All groups underwent toothbrushing simulation (60,000 cycles) and bleaching treatment (4 sessions). Mean surface roughness (Ra, µm) was measured before (T0) and after treatments (TB). Surface morphology was assessed by scanning electron microscopy (SEM) at TB. Mean Ra was analyzed using general mixed models and multiple comparisons by the Tukey-Kramer test (α=5%). Results: HP caused no surface roughness changes on the nanofilled composite after treatment (p>0.05). RT toothbrushing, combined or not with HP, increased the surface roughness (p<0.05). WT and WT/ HP protocols had no effect on the surface roughness of the composite (p>0.05). The nanofilled composite submitted to RT toothbrushing combined with HP (RT/HP) presented substantial surface alterations under SEM, showing deep depressions and round-shaped defects. Toothbrushing with RT combined with the bleaching agent increased exposure of the inorganic fillers. Conclusion: WT toothbrushing, regardless of HP combination, or the single HP protocol had no effect on the surface roughness of the nanofilled composite. However, RT combined with HP negatively affected surface roughness and presented the most noticeable surface changes among groups

Effect of chemical or mechanical finishing/polishing and immersion in staining solutions on the roughness, microhardness, and color stability of CAD-CAM monolithic ceramics / Efeito do acabamento/polimento químico ou mecânico e imersão em soluções manchantes na rugosidade, microdureza e estabilidade da cor em cerâmicas monolíticas CAD-CAM

ABSTRACT During the manufacture of ceramic restorations there is an important step of finishing and polishing and the effects of different types of these procedures on the surface characteristics of ceramics are not known for sure. Aim: To evaluate the effects of various surface treatments and immersion in coloring substances on the roughness, microhardness, and color stability of CAD-CAM monolithic ceramics. Materials and Method: The ceramics used were lithium disilicate reinforced with zirconium dioxide (Suprinity), lithium disilicate (E.max) or leucite (Empress). They were subjected to two surface treatments: glazing (group G) (n=20) or mechanical polishing (group P) (n=20). Then they were divided into two subgroups (n=10) to be treated with the staining substance (coffee or water). Roughness, microhardness and color were measured before and after treatment. Data were subjected to analysis of variance and multiple comparisons were performed with Tukey tests at 5% significance level. Results: Roughness was lower in all tested ceramics after polishing than after glazing. Microhardness was the same for polished and glazed E.max, higher in glazed than polished Empress, and higher in polished than glazed Suprinity. Analysis of the effects of glazing and polishing on the individual ceramics showed that the ΔE2000 and ΔWID data of the E.max ceramic subjected to polishing showed greater change. Mechanical polishing is a good option for surface treatment of monolithic ceramics. Conclusion: Glazing was inferior and less satisfactory than polishing. Glazing generates changes that can lead to color instability.

RESUMO Durante a confecção de restaurações cerâmicas existe uma importante etapa dos procedimentos de acabamento e polimento. Os efeitos de diferentes tipos desses procedimentos nas características superficiais das cerâmicas não são conhecidos com certeza. Objetivo: Avaliar os efeitos de vários tratamentos de superfície e imersão em substâncias corantes na rugosidade, microdureza e estabilidade de cor de cerâmicas monolíticas CAD-CAM. Materiais e Métodos: As cerâmicas utilizadas foram dissilicato de lítio reforçado com dióxido de zircônio (Suprinity), dissilicato de lítio (E.max) ou leucita (Empress). Foram submetidos a dois tratamentos de superfície: glazeamento (grupo G) (n=20) ou polimento mecânico (grupo P) (n=20). Em seguida, foram divididos em dois subgrupos (n=10) para serem tratados com a substância corante (café ou água). Rugosidade, microdureza e cor foram medidas antes e após o tratamento. Os dados foram submetidos à análise de variância e as comparações múltiplas foram realizadas com testes de Tukey ao nível de 5% de significância. Resultados: A rugosidade foi menor em todas as cerâmicas testadas após o polimento do que após o glazeamento. A microdureza foi a mesma para o E.max polido e vidrado, maior no Empress vidrado do que no polido, e maior no Suprinity polido do que no vidrado. A análise dos efeitos do esmaltação e polimento nas cerâmicas individuais mostrou que os dados ΔE2000 e ΔWID da cerâmica E.max submetida ao polimento apresentaram maior alteração. O polimento mecânico é uma boa opção para o tratamento superficial de cerâmicas monolíticas. Conclusão: A aplicação do glazing foi inferior e menos satisfatório que o polimento, gerando alterações que podem levar à instabilidade da cor.

Effect of endodontic sealers on push-out bond strength of CAD-CAM or prefabricated fiber glass posts

Abstract This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used. In the half to receive milled-CAD-CAM posts, tooth specimens were molded with acrylic resin to obtain replicas. These were scanned to enable the laboratory to produce the milled-CAD-CAM GFPs (Fiber CAD Lab, Angelus) by the subtractive technique. The other half of samples received prefabricated GFPs (Exacto, Angelus) (n=15). The GFPs were cemented with dual-cure resin cement (Panavia F2.0, Kuraray). Each root was sectioned into two slices per root region (cervical, middle, apical) that were subjected to the push-out BS test, in a universal testing machine. Failure mode (FM) was classified by scores. The BS data were submitted to generalized linear model analyses, while FM was analyzed using the chi-square test (a=0.05). BS showed no significant difference among the three ES (p > 0.05). BS was significantly higher for prefabricated (mean 10.84 MPa) versus milled-CAD-CAM GFPs (mean 6.94 MPa) (p <0.0001), irrespective of ES. The majority showed mixed failures. It could be concluded that type of ES did not affect BS of GFPs to dentin, and prefabricated-GFPs had higher bond-strength than customized-milled-CAD-CAM GFPs.

Dentin permeability after pretreatment with titanium tetrafluoride and self-etching or universal adhesive systems

Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer's instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used

Antifungal analysis of incorporation of the essential oil of Cymbopogon citratus (D.C.) Stapf into polymethyl methacrylate / Análise antifúngica da incorporação do óleo essencial de Cymbopogon citratus (d.c.) Stapf em polimetacrilato de metila

ABSTRACT Objective: Evaluated the antifungal effect of the incorporation of different concentrations of the essential oil Cymbopogon citratus (capim santo), into polymethylmethacrylate (PMMA) against Candida albicans. Methods: Fifty specimens were fabricated and divided into five groups: Group 1, PMMA + 10% essential oil (n=10); Group 2, PMMA + 15% essential oil (n=10); Group 3, PMMA + 20% essential oil (n=10); Group 4, PMMA + 25% essential oil (n=10); Group 5, PMMA (n=10). PMMA powder was mixed with the monomer and the mixture was placed in disc-shaped cavities measuring 15 mm in diameter, 2 mm thick. To evaluate the antifungal activity of the experimental specimens, the standard strain of Candida albicans was tested. After incubation, the colony count of each plate was performed using a digital colony counter, obtaining the number of colony forming units (CFU) and the Kruskal-Wallis test was applied. Results: There was statistically significant difference in the CFU count of Candida albicans as a consequence of the addition of Cymbopogon citratus essential oil to PMMA (p < 0.001) and values were significantly higher in comparison with those of all the other groups, when the essential oil was incorporated as incorporated into the PMMA in the concentration of 20%. In the other concentrations, no difference in values was observed in comparison with the Control Group without essential oil of Cymbopogon citratus. Conclusion: The acrylic resin with the essential oil incorporated into it in different concentrations provided no effect against development of the genus Candida.

RESUMO Objetivo: Avaliar o efeito antifúngico da incorporação de diferentes concentrações do óleo essencial Cymbopogon citratus (capim santo), em polimetilmetacrilato (PMMA) contra Candida albicans. Métodos: Cinquenta corpos de prova foram confeccionados e divididos em cinco grupos: Grupo 1, PMMA + 10% de óleo essencial (n=10); Grupo 2, PMMA + 15% de óleo essencial (n=10); Grupo 3, PMMA + 20% de óleo essencial (n=10); Grupo 4, PMMA + 25% de óleo essencial (n=10); Grupo 5, PMMA (n=10). O pó de PMMA foi misturado ao monômero e a mistura foi colocada em cavidades em forma de disco medindo 15 mm de diâmetro por 2 mm de espessura. Para avaliar a atividade antifúngica dos espécimes experimentais, foi testada a cepa padrão de Candida albicans. Após a incubação, foi realizada a contagem de colônias de cada placa por meio de um contador digital de colônias, obtendo-se o número de unidades formadoras de colônias (UFC) e para isso foi aplicado o teste de Kruskal-Wallis. Resultados: Houve diferença estatisticamente significativa na contagem de UFC de Candida albicans como consequência da adição do óleo essencial de Cymbopogon citratus ao PMMA (p < 0,001) e os valores foram significativamente maiores em comparação com todos os outros grupos, quando o essencial óleo foi incorporado como incorporado ao PMMA na concentração de 20%. Nas demais concentrações, não houve diferença nos valores em relação ao Grupo Controle sem óleo essencial de Cymbopogon citratus. Conclusão: A resina acrílica com o óleo essencial incorporado a ela em diferentes concentrações não apresentou efeito contra o desenvolvimento do gênero Candida.

Effect of thermocycling on internal microhardness of high and low viscosity bulk fill composite resins in class I cavities / Efeito da termociclagem na microdureza interna de resinas compostas bulk fill de alta e baixa viscosidade aplicadas em cavidades classe I

ABSTRACT Objective: To evaluate the effect of thermocycling on the Knoop internal microhardness of high- and low viscosity bulk fill resins applied in Class I cavities. Methods: Thirty third molars with Class I cavity preparations were randomly divided into 3 groups according to the restorative system: nanoparticulated composite resin (Filtek™ Z350 XT 3M ESPE) (oblique increments of 2mm); low viscosity bulk fill resin (Filtek™ Bulk fill Flow, 3M ESPE) (3mm increments covered with a 1-mm layer of nanoparticulated resin); high viscosity bulk fill resin (Filtek™ Bulk fill, 3M ESPE) (single 4-mm increment). After 24h, half of samples was submitted to thermocycling (1,000 cycles). All samples (n=5) were sectioned in half to measure the internal microhardness at bottom and top of restoration. Results: Analysis of variance indicated that, for nanoparticulated composite resin, without thermocycling, the microhardness at the top was statistically lower than at the bottom. After thermocycling, there was no difference in microhardness between the top and the bottom. For low viscosity bulk fill resin, without thermocycling, there was no significant difference in microhardness means between the top and the bottom. After thermocycling, significantly higher microhardness was found at the top than at the bottom (p <0.05). For high viscosity bulk fill resin there was no significant difference between the microhardness values at the top and bottom, regardless of thermocycling (p> 0.05). In all composite resins, an increase in microhardness was observed after thermocycling (p <0.05). Conclusion: Thermocycling increased the internal microhardness of resin restorations, and, for the low viscosity bulk fill resin, the microhardness at the top was higher than at the bottom after thermocycling.

RESUMO Objetivo: Avaliar o efeito da termociclagem na microdureza Knoop interna de resinas bulk fill de alta e baixa viscosidade aplicadas em cavidades classe I. Métodos: Trinta terceiros molares com cavidades Classe I foram divididos aleatoriamente em três grupos de acordo com o sistema restaurador: Resina composta nanoparticulada (Filtek™ Z350 XT 3M ESPE) (incrementos oblíquos de 2mm); resina bulk fill de baixa viscosidade (Filtek™ Bulk fill Flow, 3M ESPE) (incremento de 3mm mais 1mm de resina nanoparticulada); resina bulk fill de alta viscosidade (Filtek ™ Bulk fill, 3M ESPE) (único incremento de 4mm). Após 24h, metade das amostras foi submetida a termociclagem (1.000 ciclos). Todas as amostras (n=5) foram seccionadas ao meio para mensuração da microdureza interna na base e topo da restauração. Resultados: Análise de variância indicou que, para a resina composta nanoparticulada e antes da termociclagem, a microdureza no topo foi estatisticamente inferior do que na base (p<0,05). Após a termociclagem, não houve diferença entre topo e base. Já para a resina bulk fill de baixa viscosidade, antes da termociclagem, não se constatou diferença significativa nos valores de microdureza entre topo e base. Após termociclagem, valores significativamente mais elevados de microdureza foram encontrados no topo do que na base (p<0,05). Para resina bulk fill de alta viscosidade, não houve diferença significativa na microdureza entre topo e base, realizando-se ou não termociclagem (p>0,05). Em todas as resinas compostas foi verificado aumento de microdureza após termociclagem (p<0,05). Conclusão: A termociclagem aumentou a microdureza para todas as resinas compostas, sendo que para a resina bulk fill de baixa viscosidade a microdureza no topo foi maior do que na base após termociclagem.

Bonding strategy of a universal adhesive system containing chitosan: influence on dentin permeability, and effect on adhesive layer micromorphology / Estratégia de união de um sistema adesivo universal contendo quitosana: influência na permeabilidade dentinária e efeito na micromorfologia da camada do adesivo

ABSTRACT Aim: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. Materials and Method: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. Results: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. Conclusions: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.

RESUMO Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levo

Influence of restorative materials on occlusal and internal adaptation of CAD-CAM inlays

Aim: To evaluate the occlusal and internal marginal adaptation of inlay restorations made of different materials, using CAD-CAM. Methods: Preparations were made for MOD inlays of one-third intercuspal width and 4 mm depth in 30 third human molars. The teeth were restored using CAD-CAM materials (n=10) of nanoceramic resin (Lava Ultimate), polymer-infiltrated ceramic network (VITA ENAMIC), or lithium disilicate glass-ceramic (IPS e.max CAD). The specimens were cemented with dual resin cement and sectioned at the center of the restoration, after which the two halves were evaluated, and photographed The occlusal and internal discrepancy (µm) was determined at five points: cavosurface angle of the occlusal-facial wall (CA-O); center of the facial wall (FW); faciopulpal angle (FPA); center of the pulpal wall (PW); and center of the lingual wall (LW). The data were submitted to the Kruskal-Wallis and the Dunn tests (α=0.05). Results: No difference was observed among the materials regarding the occlusal discrepancy at the CA-O, FPA, or PW internal points. The e.max CAD measurement at FW showed larger internal discrepancy than that of Lava (p=0.02). The internal discrepancy at LW was greater for e.max CAD than VITA ENAMIC (p=0.02). Conclusion: Lithium disilicate glass-ceramic presented greater internal discrepancy in relation to the surrounding walls of the inlay preparations

Bulk-fill restorative composites under simulated carious and erosive conditions / Resinas compostas restauradoras bulk-fill sob condiçöes simuladas de cárie e erosão

ABSTRACT Acidic conditions can cause hydrolysis and accelerate degradation of resin composites (RCs). Since there are limited and controversial data on the effect of acids on bulk-fill RCs, this study assessed the surface roughness (SR) and flexural strength (FS) of these RCs under simulated carious and erosion conditions. Bars of Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent), and Aura Bulk Fill (ABF, SDI) and a conventional RC [Filtek Z350XT (FZ, 3M/ESPE)] were allocated (n=15) to undergo caries or erosion conditions. The control group was kept in artificial saliva (AS). The bars were evaluated for SR change (final-baseline) and for three-point FS. Data were analyzed using ANOVA and Tukey's test. At the baseline (p <0.001), the SR of RCs ranked as follows: (TBF = XTF) < FBF (none differed from FZ) < ABF. The interplay between RCs and conditions affected SR change (p = 0.025). While after storage in AS, there was no difference among RCs, following carious and erosive conditions, ABF showed higher SR change. For FS (p <0.001), XTF > (FBF = FZ) > (TBF = FZ) > ABF, with no difference among control, carious and erosive conditions (p = 0.148). Depending on the restorative bulk-fill RCs, carious and erosive conditions roughen the surface but do not affect the FS of these materials.

RESUMO Condições acídicas podem causar hidrólise e acelerar a degradação de resinas compostas (RCs). Como há dados limitados e controversos sobre os efeitos de ácidos sobre RCs bulk-fill, este estudo avaliou a rugosidade de superfície (RS) e a resistência flexural (RF) dessas RCs sob condições simuladas de cárie e erosão. Barras de Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent) e Aura Bulk Fill (ABF, SDI) e de uma RC convencional [Filtek Z350XT (FZ, 3M/ESPE)] foram alocadas (n=15) para estarem sob condições cariogênicas ou erosivas. O grupo controle foi mantido em saliva artificial saliva (SA). As barras foram avaliadas quanto à alteração de RS (final-inicial) e à RF de três pontos. Os dados foram analisados utilizando ANOVA e teste de Tukey. Inicialmente (p <0,001) a RS das RCs foi a seguinte: (TBF = XTF) < FBF (nenhuma diferiu de FZ)< ABF. A interação entre as RCs e as condições acídicas influenciou a alteração de RS (p = 0,025). Após armazenamento na SA, não houve diferença entre as RCs, enquanto após condições cariogênicas e erosivas a ABF mostrou a maior alteração de RS. Para FS (p < 0,001), XTF > (FBF = FZ) > (TBF = FZ) >ABF, sem diferença entre controle e condições cariogênicas e erosivas (p = 0,148). Dependendo da RC bulk-fill restauradora, condições cariogênicas e erosivas aumentam a RS, mas não alteram a RF desses materiais.

Effect of acid challenge and photoactivation distance on microhardness and roughness of flow bulk-fill composite resins / Efeito do desafio ácido e distância de fotoativação na microdureza e rugosidade de resinas compostas bulk-fill flow

Abstract Introduction composite resins are indicated to the reconstruction of proximal walls and the evaluation of properties of flow bulk-fill composite resins exposed to acid challenge is necessary. Objective to evaluate the microhardness and roughness at different depths of photoactivation of bulk-fill flow composites (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) and conventional composite resin (control, Filtek Z350 XT) subjected to acid challenge. Material and method forty composites brick shaped specimens (3x3x4 mm) were made using a polyacetal matrix. To simulate pH challenges, the samples were immersed in a demineralizing solution. Each sample had Knoop microhardness (KHN) and roughness (Ra) evaluated at three depths (superficial, medium, and cervical), considering the lateral surface of the sample. Data were submitted to Kruskal-Wallis, Friedman's and Dunn's tests with a significance level of 5%. Result comparing the composites among themselves, in superficial (p=0.693), medium (p=0.053) and cervical (p=0.176) regions, there was no difference in the KHN values. There were also no differences in roughness between the composites in superficial (p=0.356), medium (p=0.734) and cervical (p=0.207) regions. Only the Filtek Z350 XT (p=0.027) showed less difference in KHN in the middle region caused by acid challenge. Changes in roughness showed that the greatest difference was at the cervical region for Bulk Fill Flow SDR (p=0.014) and Tetric N-Ceram Bulk Fill (p = 0.003) with an increase after acid challenge. Conclusion after acid challenge, bulk-fill flow composites showed alterations similar to those presented by the conventional nanoparticulate resin composite.

Resumo Introdução as resinas compostas são indicadas para reconstrução de paredes proximais e a avaliação das propriedades das resinas compostas bulk-fill flow expostas ao desafio ácido mostra-se necessária. Objetivo avaliar a microdureza e rugosidade em diferentes profundidades de fotoativação de resinas compostas bulk-fill flow (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) e convencional (controle, Filtek Z350 XT) submetidas ao desafio ácido. Material e método quarenta amostras retangulares (3x3x4 mm) foram confeccionadas utilizando uma matriz de poliacetal. Para simular o desafio ácido, as amostras foram imersas em uma solução desmineralizante. Cada amostra teve a microdureza Knoop (KHN) e rugosidade (Ra) avaliadas em três profundidades (superficial, média e cervical), considerando a superfície lateral da amostra. Os dados foram submetidos aos testes de Kruskal-Wallis, Friedman e Dunn com nível de significância de 5%. Resultado comparando as resinas compostas entre si, nas regiões superficial (p=0,693), média (p=0,053) e cervical (p=0,176), não houve diferença nos valores de KHN. Também não houve diferenças na rugosidade entre os materiais nas regiões superficial (p=0,356), média (p=0,734) e cervical (p=0,207). Apenas o Filtek Z350 XT (p=0,027) apresentou menor diferença de KHN na região intermediária causada pelo desafio ácido. As mudanças na rugosidade mostraram que a maior diferença foi na região cervical para Bulk Fill Flow SDR (p=0,014) e Tetric N-Ceram Bulk Fill (p=0,003), com aumento após o desafio ácido. Conclusão após desafio ácido, as resinas compostas bulk-fill flow apresentaram alterações semelhantes às apresentadas pela resina composta convencional nanoparticulada.

Influence of fluoride-releasing materials in the inhibition of enamel and dentin demineralization around restorations / Influência de materiais liberadores de flúor na inibição da desmineralização do esmalte e da dentina ao redor de restaurações

Objective: The aim was to evaluate the influence of fluoride-releasing restorative materials in enamel and dentin microhardness. Material and Methods: 40 blocks (5x5x3 mm) from cervical third of human molars received a cavity preparation between the enamel and dentin, and the restorations were subjected to in vitro caries model. Specimens were randomly restored with (n=10): conventional glass ionomer cement (Ketac Cem, 3M ESPE); polyacid-modified composite resin (Ionoseal, VOCO); resin-modified glass ionomer cement (Ionofast, Biodinâmica); or microhybrid composite resin (Filtek Z250, 3M ESPE). The specimens were sectioned longitudinally and enamel and dentin Knoop microhardness were determined at different distances from the restorative material (100, 200 and 300 µm) and depth of surface (20, 40 and 60 µm). The data were submitted to three-way repeated measures ANOVA and Tukey ́s test ( α =0.05). Results: For enamel, the double interactions between material x distance and material x depth were statistically significant. In all depths and distances, the highest values of enamel microhardness were observed for Ketac Cem. In dentin, the materials differed statistically from each other, and Ionoseal obtained higher microhardness values than those found in Ionofast. Conclusion: Conventional glass ionomer cement is more effective in preventing enamel demineralization around restoration followed by the polyacid-modified composite resin. In dentin, the polyacid-modified composite resin obtained better performance than resin-modified glass ionomer cement. (AU)

Objetivo: O objetivo foi avaliar a influência de materiais restauradores liberadores de flúor na microdureza do esmalte e da dentina. Material e Métodos: 40 blocos (5x5x3 mm) do terço cervical de molares humanos receberam preparo cavitário entre esmalte e dentina, e após a restauração foram submetidas a um modelo in vitro de cárie. As amostras foram restauradas aleatoriamente com (n=10): cimento de ionômero de vidro convencional (Ketac Cem, 3M ESPE); resina composta modificada por poliácidos (Ionoseal, VOCO); cimento de ionômero de vidro modificado por resina (Ionofast, Biodinâmica); ou resina composta microhíbrida (Filtek Z250, 3M ESPE). As amostras foram seccionadas longitudinalmente e a microdureza Knoop de esmalte e dentina foi determinada em diferentes distâncias do material restaurador (100, 200 e 300 µm) e profundidade de superfície (20, 40 e 60 µm). Os dados foram submetidos à ANOVA para medidas repetidas de três fatores e teste de Tukey (α =0,05). Resultados: Para o esmalte, as duplas interações entre material x distância e material x profundidade foram estatisticamente significativas. Em todas as profundidades e distâncias, os maiores valores de microdureza do esmalte foram observados para o Ketac Cem. Na dentina, Ionoseal obteve valores de microdureza superiores aos encontrados no Ionofast. Conclusão:O cimento de ionômero de vidro convencional é mais eficaz na prevenção da desmineralização do esmalte ao redor da restauração, seguido pela resina composta modificada por poliácidos. Na dentina, a resina composta modificada por poliácidos obteve melhor desempenho que o cimento de ionômero de vidro modificado por resina. (AU)

Diagnostic methods for stained pits and fissures caries lesions on the occlusal surface / Métodos diagnósticos para lesões de cárie com sulcos pigmentados em superfície oclusal

ABSTRACT Objective: The aim of this study was to compare methods for in vitro diagnosis of pigmented pits and fissures on the occlusal surface. Methods: Forty-one human molars and premolars extracted with pigmentation in pits and fissures were used. The teeth were evaluated with artificial illumination for classification according to ICDAS, followed by fluorescent laser evaluation. For the radiographic evaluation, the teeth were positioned to obtain interproximal images, adopting the criterion of Rodrigues et al. 2008 for diagnosis of lesions. For histological evaluation, the teeth were sectioned in the mesiodistal direction in the occlusal sulcus region and evaluated in a 20-fold stereoscopic magnifying glass, using the criterion of Ekstrand et al. (1997) for evaluation. The methods were compared with the histological evaluation, obtaining values of accuracy, sensitivity and specificity regarding the response variables "presence / absence" of enamel caries. Results: When comparing visual inspection with histological analysis, 65.85% accuracy, 40% sensitivity and 90.48% specificity were observed with false positive and negative probability of 20% and 38.71%. When comparing the fluorescent laser with the histological analysis, the accuracy was 58.54%, sensitivity 70% and specificity 47.62%. Comparing the radiographic analysis with the histological analysis, it was obtained 53.66% accuracy, sensitivity of 42.11% and specificity of 73.68%. Conclusion: The ROC curve and the Yuden index showed that visual inspection presented the best combination of sensitivity and specificity than fluorescent laser and radiographic analysis for diagnosis, which represented the best method for detecting inactive carious lesions in enamel.

RESUMO Objetivo: O objetivo deste estudo foi comparar métodos para diagnóstico in vitro de sulcos pigmentados em superfície oclusal. Métodos: Foram utilizados 41 molares e pré-molares humanos extraídos com pigmentação em sulcos e fissuras. Os dentes foram avaliados com iluminação artificial para classificação quanto ao critério ICDAS, seguida por avaliação com laser fluorescente. Para a avaliação radiográfica, os dentes foram posicionados para obtenção de imagens interproximais, adotando-se o critério de Rodrigues et al. (2008) para diagnóstico. Para avaliação histológica, os dentes foram seccionados no sentido mésio-distal na região de sulco oclusal e avaliados em lupa estereoscópica com aumento de 20 vezes, adotando-se o critério de Ekstrand et al. (1997). Os métodos foram comparados com a avaliação histológica, obtendo-se valores de acurácia, sensibilidade e especificidade quanto às variáveis de resposta "presença/ausência" de lesão de cárie em esmalte. Resultados: Ao comparar a inspeção visual com a análise histológica, observou-se acurácia de 65,85%, sensibilidade de 40% e especificidade de 90,48%. Ao comparar o laser fluorescente com a análise histológica, a acurácia foi de 58,54%, sensibilidade de 70% e especificidade de 47,62%. Na comparação da análise radiográfica com a histológica, obteve-se acurácia de 53,66%, sensibilidade de 42,11% e especificidade de 73,68%. Conclusão: A curva ROC mostrou que a inspeção visual apresentou a melhor combinação de sensibilidade e especificidade que o laser fluorescente e que a análise radiográfica para o diagnóstico, representando o melhor método para detecção de cárie em lesões com sulcos pigmentados em esmalte

Effects of ionizing radiation and different resin composites on shear strength of ceramic brackets: an in vitro study

ABSTRACT Introduction: Head and neck cancer is considered one of the most common types, and its treatment includes radiotherapy, which can trigger side effects and undesirable sequelae in the oral cavity and dental tissues. Objective: This study aimed to make an in vitro evaluation of the shear strength and failure mode of ceramic orthodontic brackets bonded with two different composites in enamel submitted to ionizing radiation. Methods: After the study was approved by the Research Ethics Committee, 60 healthy human premolars were selected and divided into two groups, based on the absence or presence of ionizing irradiation of the enamel. The fragments were thermocycled and then randomly subdivided into two subgroups, according to the composite used for bonding the ceramic brackets (Inspire Ice - Ormco) to the enamel (n = 15): Transbond XT composite (3M), and Light Bond composite (Reliance). After 24 hours, the specimens were submitted to the shear strength test, and the failure mode was analyzed using a stereomicroscope and confocal microscopy. The shear strength data were submitted to two-way ANOVA, considering a significance level of 5%. Results: The groups submitted to radiation presented lower shear strength values (4.48MPa) than those not irradiated (9.23MPa) (p< 0.001), and the tested composites were not statistically different (p= 0.078). Regarding the fracture mode, all the groups presented mostly adhesive fractures. Conclusion: It was concluded that ionizing radiation negatively affects the adhesion of ceramic brackets, regardless of the composite used for bonding.

Influence of calcium lactate and sodium fluoride solution mouthwashes on enamel microhardness and dentin permeability during in-office bleaching / Influência das soluções enxaguatórias de lactato de cálcio e fluoreto de sódio na microdureza do esmalte e permeabilidade dentinária durante o clareamento em consultório

Objective: This study evaluated the influence of calcium lactate and sodium fluoride mouthwashes on enamel microhardness and dentin permeability during in-office bleaching. Material and Methods: For the microhardness evaluation, enamel blocks were randomly submitted to different treatments associated with in-office bleaching agent using 40% hydrogen peroxide (Opalescence Boost PF 40%/ Ultradent; 3 sessions x 40-minute each) (n = 10): 1) Control: application of bleaching agent; 2) Calcium lactate: 1-minute immersion before bleaching treatment; 3) Sodium fluoride: immersion for 1 minute before bleaching treatment; 4) Calcium lactate + sodium fluoride: 1 minute immersion in calcium lactate solution, followed by 1 minute immersion in sodium fluoride before bleaching treatment. Dentin discs received the same treatment protocols (n = 10) to evaluate permeability. Knoop microhardness and dentin permeability assessments were performed twice (at baseline and 48 hours after the end of bleaching treatment). Results: The generalized linear model considering the design of repeated measures over time showed that there was no significant difference between treatments (p = 0.9577) and between assessments (p = 0.3267) regarding Knoop microhardness. Kruskal Wallis and Dunn tests showed that calcium lactate immersion before bleaching treatment provided higher dentin permeability than other groups (p = 0.0009). Conclusion: The use of sodium fluoride solution and calcium lactate in association with in-office bleaching treatment did not influence the microhardness of tooth enamel, although calcium lactate may increase dentin permeability. (AU)

Objetivo: Este estudo avaliou a influência dos enxaguatórios bucais com lactato de cálcio e fluoreto de sódio na microdureza do esmalte e na permeabilidade da dentina durante o clareamento em consultório. Material e Métodos: Para avaliação da microdureza, blocos de esmalte foram submetidos aleatoriamente a diferentes tratamentos associados a agente clareador em consultório com peróxido de hidrogênio 40% (Opalescence Boost PF 40% / Ultradent; 3 sessões x 40 minutos cada) (n = 10): 1) Controle: aplicação de agente clareador; 2) Lactato de cálcio: imersão de 1 minuto antes do tratamento clareador; 3) Fluoreto de sódio: imersão por 1 minuto antes do tratamento clareador; 4) Lactato de cálcio + fluoreto de sódio: 1 minuto de imersão em solução de lactato de cálcio, seguido de 1 minuto de imersão em fluoreto de sódio antes do tratamento clareador. Os discos de dentina receberam os mesmos protocolos de tratamento (n = 10) para avaliar a permeabilidade. As avaliações da microdureza Knoop e da permeabilidade dentinária foram realizadas duas vezes (no início do estudo e 48 horas após o término do tratamento clareador). Resultados: O modelo linear generalizado considerando o delineamento de medidas repetidas ao longo do tempo mostrou que não houve diferença significativa entre os tratamentos (p = 0,9577) e entre as avaliações (p = 0,3267) em relação à microdureza Knoop. Os testes de Kruskal Wallis e Dunn mostraram que a imersão de lactato de cálcio antes do tratamento clareador proporcionou maior permeabilidade dentinária do que os outros grupos (p = 0,0009). Conclusão: O uso de fluoreto de sódio e lactato de cálcio associado ao clareamento em consultório não influenciou a microdureza do esmalte dentário, embora o lactato de cálcio possa aumentar a permeabilidade dentinária (AU)

Effect of different concentrations of green tea extract solutions on bonding durability of etchand- rinse adhesive system to caries affected dentin

Aim: The in vitro study evaluated the effect of different concentrations of green tea extract solution (GT) on the bonding durability of etch-and-rinse adhesive system to caries dentin affected (CAD). Methods: Dentinal surfaces of human third molars were polished and submitted to a microbiological caries induction protocol for 14 days. After removal of the infected dentin layer, the samples were randomly divided into 4 groups (n= 10), according to the concentration of GT solution applied in CAD, after acid etching: 0.05%; 0.2%; 2% and NT (no treatment ­ control). After application of a etch-and-rinse adhesive system (Adper Single Bond 2, 3M ESPE), composite resin restorations were performed on the dentin. After 24 hours, the resin-dentin blocks were sectioned 1mm2 specimens, which were subjected to the microtensile test immediately or after 6 months of storage in water. Data were submitted to two-way ANOVA for randomized blocks and Tukey test (α= 5%). Results: There was no effect of double interaction (p= 0.934). The application of 0.2% GT promoted a statistically significant increase in dentin bond strength values in comparison to the condition where GT was not used (p=0.012). There was a significant decrease of bond strength after 6 months of storage, regardless of dentin pretreatment (p = 0.007). The G test identified that there was no statistical difference regarding failure mode (p= 0.326). Conclusion: The concentration of 0.2% improved the bond strength of an etch-and-rinse adhesive system to caries affected dentin, however, none of dentin pretreatments could prevent the decrease in bond strength over time

Low- and high-viscosity bulk-fill resin composites / Resinas compostas bulk-fill de baixa e alta viscosidade

ABSTRACT The aim of this study was to compare low- and high-viscosity bulk-fill composites for Knoop microhardness (KHN), microtensile bond strength (MTBS) to dentin in occlusal cavities, and fracture strength (FS) in molars with mesialocclusal- distal restoration. Disk-shaped samples with different thicknesses (2 or 4 mm) of low-viscosity (SDR Flow, Dentsply) and high-viscosity bulk-fill composites (Filtek BulkFill, 3M ESPE; and Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) were prepared for top and bottom KHN analysis (n=10). MTBS to dentin and fracture pattern was evaluated in human molars with occlusal cavities restored with (n=10): conventional nanocomposite (Z350XT, 3M ESPE), low-viscosity (Filtek Bulk-fill Flow, 3M ESPE) or high-viscosity bulk-fill composites (Filtek BulkFill). The FS and fracture pattern of human molar with mesial-occlusal-distal restorations submitted or not to thermomechanical cycling were investigated (n=10) using: intact tooth (control), and restoration based on conventional microhybrid composite (Z250, 3M ESPE), low-viscosity (SDR Flow) or high-viscosity bulk-fill composites (Filtek BulkFill). The data were submitted to split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) followed by Tukey's test (α=0.05). For KHN, there was no significant difference for the resin composites between the top and bottom. For MTBS, no significant differences among the materials were detected; however, the low-viscosity composite presented lower frequency of adhesive failures. For FS, there was no significant difference between composites and intact tooth regardless of thermomechanical cycling. Low- and high-viscosity bulk-fill composites have comparable microhardness and microtensile bond strength when used in occlusal restorations. Likewise, the bulk-fill composites present similar fracture strength in molars with mesio-occlusal-distal restorations.

RESUMO O objetivo deste estudo foi comparar resinas compostas bulk- -fill de baixa e alta viscosidade quanto à microdureza Knoop (KHN), resistência de união a microtração (MTBS) em cavidades oclusais e carga à fratura (FS) em molares com restauração mesio-oclusal-distal. Amostras em forma de disco com diferentes espessuras (2 ou 4 mm) de resinas bulk-fill de baixa viscosidade (SDR Flow, Dentsply) e alta viscosidade (Filtek BulkFill, 3M ESPE; e Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) foram obtidas para análise de KHN no topo e na base (n = 10). A MTBS em dentina e o padrão de fratura foram avaliados em molares humanos com cavidades oclusais restauradas com (n = 10): resina composta nanoparticulada convencional (Z350XT, 3M ESPE), resinas bulk-fill de baixa viscosidade (Filtek Bulk-fill Flow, 3M ESPE) ou alta viscosidade (Filtek BulkFill). Foram investigados a FS e o padrão de fratura de molares humanos em restaurações mesial-ocluso-distais sub metidas ou não à ciclagem termomecânica (n = 10), sendo: dente íntegro (controle), e restaurações baseadas em resina composta microhíbrida convencional (Z250, 3M ESPE); resinas bulk-fill de baixa viscosidade (SDR Flow) ou alta viscosidade (Filtek BulkFill). Os dados foram submetidos a split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) seguidos do teste de Tukey (α = 0,05). Para KHN, não houve diferença significativa entre o topo e a base para as resinas compostas. Para MTBS, não foram detectadas diferenças significativas entre os materiais; entretanto, a resina bulk-fill de baixa viscosidade apresentou menor frequência de falhas adesivas. Para FS, não houve diferença significativa entre os materiais e o dente íntegro, independentemente da ciclagem termomecânica. As resinas bulk-fill de baixa e alta viscosidade têm microdureza e resistência à microtração comparáveis quando usados em restaurações oclusais. Da mesma forma, as resinas bulk-fill apresentam resistência à fratura semelhante em molares com restaurações mesio-oclusal-distais.

Effect antioxidants application on microshear bond strength of universal adhesive to bleached enamel / Efeito da aplicação de antioxidantes na resistência de união do adesivo universal ao esmalte clareado

Purpose: To evaluate, in vitro, the influence of antioxidants (green tea extract - GT and sodium ascorbate - SA) on microshear bond strength (µSBS) of a universal adhesive system ­ self-etching mode (UAS) to bleached enamel. Material and Methods: After obtaining 50 fragments of human dental enamel (4 mm x 4 mm), forty fragments were submitted to at-home bleaching technique using 10% carbamide peroxide (Opalescence PF, Ultradent) for two h/day, for four weeks. They were randomly divided in four groups (n = 10): GT - 10% aqueous GT solution (60 min); SA - 10% SA solution (10 min); Negative control - no antioxidant agent, immediately restored; PC1 (positive control 1) - no antioxidant agent, restored 14 days the bleaching procedure. Ten enamel fragments were assigned to PC2 group (positive control 2), in which the adhesive procedures were realized in non-bleached enamel. The UAS (Adper Single Bond Universal, 3M ESPE) was applied on enamel surface according to manufacturer's instructions and two cylinders (0.8 mm diameter) of nanoparticulate composite resin (Z350, 3M ESPE) were made on each sample. After 24 h, the cylinders were submitted to µSBS in a universal test machine (0.5 mm/min). Fracture mode was evaluated in stereomicroscope (30x magnification). SBS data, in MPa, was submitted to one-way ANOVA and fracture mode to Chi-square test (α = 0.05). Results: There was no statistical difference between the experimental groups (p = 0.545) and fracture mode (p = 0.16424). There was predominance of adhesive fracture in all groups. Conclusion: Neither the bleaching procedure nor the application of antioxidants to bleached enamel interfered in the bond strength of the tested universal adhesive system (AU)

Objetivo: Avaliar, in vitro, a influência de antioxidantes (extrato de chá verde - GT e ascorbato de sódio - SA) na resistência de união ao microcisalhamento (µSBS) de um sistema adesivo universal - modo de autocondicionamento (UAS) ao esmalte clareado. Material e Métodos: Realizou-se a obtenção de 50 fragmentos de esmalte dental humano (4 mm x 4 mm), sendo que desses, quarenta fragmentos foram submetidos à técnica de clareamento caseiro utilizando peróxido de carbamida a 10% (Opalescence PF, Ultradent) por duas horas/dia, durante quatro semanas. Eles foram divididos aleatoriamente em quatro grupos (n= 10): Expostos a GT - solução aquosa de GT a 10% (60 min); expostos a SA - solução 10% SA (10 minutos); Sem exposição ao agente antioxidante e imediatamente restaurado - (controle negativo); Sem exposição ao agente antioxidante e restaurado 14 dias após o clareamento - PC1 (controle positivo 1). Os dez fragmentos de esmalte restantes foram atribuídos ao grupo PC2 (controle positivo 2), no qual os procedimentos adesivos foram realizados em esmalte não clareado. O UAS (Adper Single Bond Universal, 3M ESPE) foi aplicado na superfície do esmalte de acordo com as instruções do fabricante e dois cilindros (0,8 mm de diâmetro) de resina composta nanoparticulada (Z350, 3M ESPE) foram feitos em cada amostra. Após 24 h, os cilindros foram submetidos ao µSBS em uma máquina de teste universal (0,5 mm/min). O modulo de fratura foi avaliado em estereomicroscópio (aumento de 30x). Os dados do SBS, em MPa, foram submetidos à ANOVA unidirecional e ao modo fratura ao teste do qui-quadrado (α = 0,05). Resultados: Não houve diferença estatística entre os grupos experimentais (p = 0,545) e modulo de fratura (p = 0,16424). Houve predomínio de fratura adesiva em todos os grupos. Conclusão: Nem o procedimento de clareamento nem a aplicação de antioxidantes no esmalte clareado interferiram na resistência de união do sistema adesivo universal testado. (AU)

Effect of bleaching protocols on surface roughness and color change of high- and low-viscosity bulk-fill composite resins / Efeito de protocolos clareadores na rugosidade de superfície e alteração de cor de resinas compostas bulk-fill de alta e baixa viscosidade

ABSTRACT The aim of this in vitro study was to evaluate the effect of bleaching protocols on the surface roughness (Ra), color change and surface micromorphology of a low-viscosity bulk-fill composite (Filtek Bulk Fill Flow, 3M ESPE), a highviscosity bulk-fill composite (Filtek Bulk Fill, 3M ESPE) and a conventional nanoparticulate composite resin (control) (Filtek Z350 XT, 3M ESPE). Forty samples of each composite (disks 5 mm in diameter and 2 mm thick) were randomly divided into four groups (n=10), according to bleaching protocol: a) 10% carbamide peroxide gel (Opalescence, Ultradent Products) (2 h/ day, for 14 days); b) 40% hydrogen peroxide gel (Opalescence Boost, Ultradent Products) (three bleaching sessions, once a week, 45 min/session); c) whitening rinse (Listerine Whitening Extreme, Johnson & Johnson) (2 min/day, for 14 days); and d) distilled water (control). The samples were submitted to triplicate readings (Ra and color [CIELAB parameters]) before and after contact with bleaching protocols. Micromorphology was analyzed in a scanning electron microscope (SEM). Ra and color parameters (ΔL, Δa, Δb and ΔE) were analyzed by generalized linear models (α=0.05). The Ra of the high-viscosity bulk-fill was significantly higher than that of the other composites (p<0.05). Ra increased significantly (p<0.05) and surface became more irregular (SEM analysis) in all the composite resins, regardless of the bleaching protocol (p<0.05). The high-viscosity bulk-fill composite resin group had significantly lower ΔE (p<0.05) than the nanoparticulate composite resin group immersed in distilled water. It was concluded that the characteristics of each resin significantly influenced the Ra more than the bleaching protocol. The high-viscosity bulk-fill resin presented minor color change.

RESUMO Este estudo in vitro teve objetivo de avaliar o efeito de protocolos clareadores sobre a rugosidade de superfície (Ra), alteração de cor e micromorfologia de resina bulk-fill de baixa viscosidade (Filtek Bulk Fill Flow, 3M ESPE), alta viscosidade (Filtek Bulk Fill, 3M ESPE) e de uma resina composta nanoparticulada (controle) (Filtek Z350 XT, 3M ESPE). Quarenta amostras de cada resin composta (discos de 5 mm de diâmetro e 2 mm de espessura) foram aleatoriamente divididas em quatro grupos , de acordo com protocolo clareador (n=10): a) Gel de peróxido de carbamida (Opalescence, Ultradent Products) (2 horas/dia, por 14 dias); b) Gel de peróxido de hidrogênio (Opalescence Boost, Ultradent Products) (3 sessões de clareamento, uma por semana, 45 min/sessão); enxaguatório clareador (Listerine Whitening Extreme, Johnson & Johnson) (2 min/dia, por 14 dias); d) água destilada (controle). As amostras foram submetidas a leituras, em triplicata (Ra e cor (parâmetros CIELab) antes e depois do contato com os protocolos clareadores. A micromorfologia de superfície foi conduzida em microscópio eletrônico de varredura (MEV). Ra e parâmetros de cor (ΔL, Δa, Δb e ΔE) foram analisados por modelos lineares generalizados (α=0.05). A Ra da resina bulk-fill de alta viscosidade foi significantemente superior do que para os outros compósitos (pp<0.05). A Ra aumentou significantemente (p<0.05) e a superfície ficou mais irregular (MEV) para todos os compósitos, independente do protocolo clareador (pp<0,05). A resina bulk-fill de alta viscosidade obteve menor ΔE (pp<0.05) do que a resina composta nanoparticulada, imersa em água destilada. Pode-se concluir que as características de cada resina composta influenciaram de forma mais significativa a Ra do que o protocolo clareador. A resina bulk fill de alta viscosidade apresentou menor alteração de cor.

Titanium dioxide nanotubes incorporated into bleaching agents: physicochemical characterization and enamel color change

Abstract Titanium dioxide nanotubes are nanostructures that can accelerate the oxidation reaction of bleaching procedures and promote a more effective whitening effect. Objective This study evaluated physicochemical properties of bleaching agents incorporated with titanium dioxide (TiO2) nanotubes, and the effects on tooth color change at different periods. Methodology 40 premolars were treated according to the following groups (n=10): CP - 10% carbamide peroxide (1 hour daily/21 days); CPN - CP incorporated into TiO2; HP - 40% hydrogen peroxide (three 40-minute sessions/7 days apart); HPN - HP incorporated into TiO2. Color shade was evaluated at five different periods (baseline, after 7, 14 and 21 days of bleaching, and 7 days after end of treatment) according to Vita Classical, CIELab and CIEDE2000 scales. Mean particle size (P), polydispersity (PO) and zeta potential (ZP) were evaluated using dynamic light scattering. Data on the different variables were analyzed by mixed model tests for measures repeated in time (ZP e L*), generalized linear models for measures repeated in time (P, PO, Vita Classical and b*), and Friedman and Mann-Whitney tests (a* and color change/ΔE and ΔE00). Results CP and CPN presented higher P, higher PO and lower ZP than HP and HPN (p≤0.05). All groups showed a significant decrease in Vita Classical color scores after 7 days of bleaching (p<0.05), and HPN presented a greater significant reduction than the other groups. L* increased in TiO2 presence, in all groups, without any differences (p>0.05) in bleaching time. A significant reduction occurred in the a* and b* values for all the groups, and HPN presented lower a* and b* values (p<0.05) than CPN. ΔE was clinically noticeable after 7 days, in all groups, and all groups resulted in a perceptible color change according to ΔE00. Conclusion TiO2 did not influence physicochemical properties of the bleaching agents. HPN presented more effective tooth bleaching than CPN.